Evaluation of shade matching in the repair of indirect restorative materials with universal shade composites

Abstract

Purpose To evaluate color differences in repair of indirect ceramic and resin nanoceramic CAD/CAM blocks with two universal shade composites after different surface preparations. Materials and Methods 120 samples were prepared from IPS Empress and GC Cerasmart270 CAD/ CAM blocks and thermocycled (5000 cycles, 5 degrees C-55 degrees C). Initial colors of sample surfaces were measured using a spectrophotometer. Rectangular prism-shaped cavities were prepared and repaired with Tokuyama Universal Bond/Omnichroma and G-Multiprimer/G-Premio/Essentia Universal following surface preparation with aluminum oxide, Cojet, and bioactive glass (Sylc). Repaired samples were thermocycled (5000 cycles) and color measurement was performed. Color coordinates L*a*b* were recorded, and color differences were calculated using the CIELab formula. Color differences between pre-and post-repair ( increment E1) and between post-repair and post-aging ( increment E2) were determined. Data were analyzed using Three-way ANOVA with a significance level set at p0.05). Conclusion Color match of the universal shade composites, which are preferred to increase the esthetic satisfaction and to simplify repair procedures, were found above the acceptable threshold. Post-aging color stability of universal shade composites was below the acceptable threshold.