Analysis of in-vitro reaction layers formed on plasma sprayed bioglass- titanium coatings

Abstract

Bioglass, 45S5 containing 45% SiO2, 6% P2O 5, 24.5%, CaO and 24.5% Na2O all in weight percent, was plasma sprayed onto a titanium substrate with and without 60Al2O 3 40TiO2 as a bond coating. It has been observed that there is a uniform coating layer with a thickness of 110 μm and that there was not any reaction observed at the coating-metal interface for both coating application. In vitro assessment of bio-activity was carried out by immersing in Simulated Body Fluid (SBF). Fourier transform infrared spectroscopy and thin film X-ray diffraction techniques were used to analyze the inorganic carbonate apatite layer developed on coating in an in-vitro environment. Scanning electron microscopy was used to surface characterization.