Ceramic insulation coatings on very thin nb3sn wires for lts coils

Simple item page
dc.contributor.authorArda, Lütfi
dc.contributor.authorÇakıroğlu, Ömer
dc.contributor.authorAktaş, Şahin
dc.contributor.authorIDTR122054
dc.contributor.authorIDTR166800
dc.contributor.authorIDTR3054
dc.date.accessioned2014-07-14T12:20:55Z
dc.date.accessioned2026-01-11T15:14:03Z
dc.date.available2014-07-14T12:20:55Z
dc.date.issued2009
dc.description.abstractCeramic insulation coatings on very thin Nb3Sn wires which are 0.001 mm (0.004”) in diameter were investigated by reel-to-reel sol-gel dip coating system. Varying thickness from submicron to several of microns sol-gel zirconium based ceramic coating has been successfully applied to Nb3Sn wires at the National High Magnetic Field Laboratory. Ceramic insulations were prepared using solutions of Yttrium and Zirconium based organometallic compounds. The film thickness was controlled by number of coating, withdrawal speed and solution chemistry. Crack-free, dense and ~ 546 nm coating was obtained with appropriate dilution of solutions. The surface morphologies and microstructure of all samples were characterized by ESEM, DTA, TGA and XRD. Resistance was measured using of HP 4339 A High Resistance Meter.en_US
dc.identifier.issn2146-5150
dc.identifier.urihttps://hdl.handle.net/11424/868
dc.language.isoengen_US
dc.publisherMarmara Üniversitesi Fen Bilimleri Dergisien_US
dc.subjectNb3Sn wire, Sol-gel, Y2O3-ZrO2, Insulation, LTS coilsen_US
dc.titleCeramic insulation coatings on very thin nb3sn wires for lts coilsen_US
dc.typearticleen_US
dspace.entity.typePublication

Files

Original bundle

Now showing 1 - 1 of 1
Thumbnail Image
Name:
file.pdf
Size:
346.72 KB
Format:
Adobe Portable Document Format
Download

Collections

Araştırma Çıktıları